FASA ADALAH BAGIAN HOMOGEN DARI SUATU SISTEM YANG MEMILIKI SIFAT FISIK DAN KIMIA YANG SERAGAM.
DIAGRAM FASA ADALAH SUATU GRAFIK YANG MERUPAKAN REPRESENTASI TENTANG FASA-FASA YANG ADA DALAM SUATU MATERIAL PADA VARIASI TEMPERATUR, TEKANAN DAN KOMPOSISI
SISTEM 1 KOMPONEN
. MENURUT GIBBS,
V = C – P + ϒ
DIMANA V = DERAJAT KEBEBASAN
C = JUMLAH KOMPONEN
P = JUMLAH FASA
Γ = JUMLAH BESARAN INTENSIFN YANG
MEMPENGARUHI SISTEM (P, T)
DIAGRAM PADA SATU KOMPONEN
DIAGRAM PADA DUA KOMPONEN
DIAGRAM FASA FE-FE₃C
LARUTAN PADAT
• PENGERTIAN LARUTAN PADAT TIDAK JAUH BERBEDA DENGAN LARUTAN LAIN YAITU BAHWA ATOM ATAU MOLEKUL DARI SATU KOMPONEN TERAKOMODASI DI DALAM STRUKTUR KOMPONEN YANG LAIN.
• LARUTAN PADAT BISA TERJADI SECARA SUBSITUSIONAL YAITU JIKA ATOM TERLARUT MENEMPATI POSISI ATOM PELARUT, ATAUPUN SECARA INTERSTISIAL YAITU JIKA ATOM TERLARUT MENEMPATI RUANG SELA ANTARA ATOM-ATOM PELARUT.
ADA PERSYARATAN TERTENTU YANG HARUS DIPENUHI UNTUK MENCAPAI KEADAAN SATU FASA, YANG DIKENAL SEBAGAI KAIDAH HUME-ROTHERY, YAITU:
1. PERBEDAAN UKURAN ATOM PELARUT DAN ATOM TERLARUT KURANG DARI 15%.
2. STRUKTUR KRISTAL DARI KOMPONEN TERLARUT SAMA DENGAN KOMPONEN PELARUT.
Larutan Padat
3. ELEKTRON VALENSI ZAT TERLARUT DAN ZAT PELARUT TIDAK BERBEDA LEBIH DARI SATU.
4. ELEKTRONEGATIVITAS ZAT TERLARUT DAN PELARUT KURANG-LEBIH SAMA, AGAR TIDAK TERJADI SENYAWA SEHINGGA LARUTAN YANG TERJADI DAPAT BERUPA LARUTAN SATU FASA.JIKA KAIDAH HUME-ROTHERY TIDAK TERPENUHI, MAKA YANG TERJADI BISA BERUPA CAMPURAN ATAU FASA PERALIHAN YANG MEMILIKI SUSUNAN KRISTAL BERBEDA DARI SUSUNAN KRISTAL KEDUA KOMPONEN YANG MEMBENTUKNYA.
Larutan Padat
DIAGRAM BINER
SISTEM BINER DENGAN KELARUTAN SEMPURNA
SISTEM KELARUTAN TERBATAS
PADA METALURGI FISIK, SELAIN SYSTEM BINER DENGAN KELARUTAN SEMPURNA DIKENAL JUGA SYSTEM BINER DENGAN KELARUTAN TERBATAS. PADATAN DENGAN DUA KOMPONEN YANG SALING MELARUTKAN SECARA SEMPURNA TIDAKLAH BANYAK. YANG UMUM TERJADI ADALAH LARUTAN PADAT DENGAN KELARUTAN MASING-MASING KOMPONEN SECARA TERBATAS.
SYSTEM BINER DENGAN KELARUTAN TERBATAS DAPAT DINYATAKAN DALAM
DIAGRAM EUTECTIC BINER, DAN
DIAGRAN PERITECTIC BINER.
Sistem Kelarutan Terbatas
Sistem Kelarutan Terbatas
Sistem Kelarutan Terbatas
PEMBEKUAN DAN SEGREGASI• SOLIDIFIKASI ADALAH PROSES PEMBEKUAN
MATERIAL,DIMANA TERJADI SERANGKAIAN PERUBAHAN BENTUK DAN FASA. • SOLIDIFIKASI BERTUJUAN UNTUK MEMPEROLEH SIFAT-
SIFAT TERTENTU DARI BAHAN MATERIAL TERSEBUT• SELAMA PEMBEKUAN ATOM-ATOM MENYUSUN DIRINYA
SECARA TERATUR DAN BERULANG ULANG DENGAN GAYA IKATAN YANG KUAT MEMBENTUK LOGAM PADAT.
A). DIAGRAM CONTINUOUS COOLING TRANSFORMATION (CCT)UNTUK MENGGAMBARKAN LAJU PENDINGINAN YANG TIDAK DALAM KONDISI KESEIMBANGAN PENGARUH KECEPATAN PENDINGINAN MANERUS TERHADAP STRUKTUR MIKRO YANG TERBENTUK DAPAT DILIHAT DARI DIAGRAM INI
a
cb
B). DIAGRAM TIME TEMPERATUR TRANSFORMATION (TTT)
• JIKA PENDINGINAN TERJADI LEBIH CEPAT MAKA TERJADI SEGREGASI YAITU DISTRIBUSI YANG TIDAK MERATA YANG TERJADI DI DALAM BUTIR. PADA PUSAT BUTIR YANG PERTAMA MAMBEKU AKAN KAYA OLEH BAHAN YANG MEMPUNYAI TITIK LELEH TINGGI, BAHAN YANG MEMPUNYAI TITIK LELEH RENDAH AKAN NAIK MANJAUHI PUSAT BUTIR• FENOMENA INI DISEBUT “ CORED STRUCTURE• KELEMAHAN “CORED STRUCTURE” :• Ø JIKA DIPADATKAN, AKAN CEPAT MELELEH.• Ø MENGURANGI KEKUATAN MEKANIK PADA TEMPERATUR
TINGGI.
REAKSI PERITEKTIKSISTEM EUTEKTIK SERING DIJUMPAI BILA TITIK CAIR DARI KEDUA KOMPONEN HAMPIR SAMA. TIPE KEDUA YANG PENTING PADA KONDISI TIGA FASA INVARIAN, YAITU REAKSI PERITEKTIK, ADALAH SISTEM DENGAN TITIK CAIR YANG SANGAT BERBEDA. BIASANYA REAKSI PERITEKTIK TERDAPAT PADA SISTEM YANG LEBIH RUMIT; SEPERTI SISTEM CU-ZN DENGAN RENTETAN TERDIRI DARI LIMA REAKSI PERITEKTIK.
LARUT SEMPURNA DALAM KEADAAN CAIR, LARUT SEBAGIAN DALAM KEADAAN PADAT (REAKSI PERITEKTIK)
DIAGRAM FASA AG-PT MERUPAKAN CONTOH TERBAIK YANG MEMILIKI REAKSI PERITEKTIK.PADA SISTEM INI REAKSI PERITEKTIK, L + TERJADI PADA 42,4% AG DAN T= 1186C.
REAKSI PERITEKTOID
REAKSI PERITEKTOID ADALAH REAKSI ISOTERMAL BOLAK BALIK (REVERSIBLE) ANTARA LOGAM BENTUK PADAT DAN LOGAM BENTUK PADAT LAINNYA PADA PROSES PENDINGINAN PADUAN LOGAM UNTUK MENGHASILKAN LOGAM BENTUK PADAT YANG BARU.
REAKSI-REAKSI FASA YANG UMUM TERJADI