Diagram Fasa Kel 4

24
DIAGRAM FASA KELOMPOK 4 ABDUL WAFA (333413 ABRAR MUHARMAN (3334131932 ANDRI SUBEKTI (333413 DIANNISA RACHMAWATI (333413 IQBAL AZIZ (3 33412 YURIANSYAH (333413

description

difas

Transcript of Diagram Fasa Kel 4

Page 1: Diagram Fasa Kel 4

DIAGRAM FASAKELOMPOK 4

ABDUL WAFA (333413

ABRAR MUHARMAN (3334131932

ANDRI SUBEKTI (333413

DIANNISA RACHMAWATI (333413

IQBAL AZIZ (333412

YURIANSYAH (333413

Page 2: Diagram Fasa Kel 4

FASA ADALAH BAGIAN HOMOGEN DARI SUATU SISTEM YANG MEMILIKI SIFAT FISIK DAN KIMIA YANG SERAGAM.

DIAGRAM FASA ADALAH SUATU GRAFIK YANG MERUPAKAN REPRESENTASI TENTANG FASA-FASA YANG ADA DALAM SUATU MATERIAL PADA VARIASI TEMPERATUR, TEKANAN DAN KOMPOSISI

Page 3: Diagram Fasa Kel 4

SISTEM 1 KOMPONEN

. MENURUT GIBBS,

V = C – P + ϒ

DIMANA V = DERAJAT KEBEBASAN

C = JUMLAH KOMPONEN

P = JUMLAH FASA

Γ = JUMLAH BESARAN INTENSIFN YANG

MEMPENGARUHI SISTEM (P, T)

Page 4: Diagram Fasa Kel 4

DIAGRAM PADA SATU KOMPONEN

Page 5: Diagram Fasa Kel 4

DIAGRAM PADA DUA KOMPONEN

Page 6: Diagram Fasa Kel 4

DIAGRAM FASA FE-FE₃C

Page 7: Diagram Fasa Kel 4

LARUTAN PADAT

• PENGERTIAN LARUTAN PADAT TIDAK JAUH BERBEDA DENGAN LARUTAN LAIN YAITU BAHWA ATOM ATAU MOLEKUL DARI SATU KOMPONEN TERAKOMODASI DI DALAM STRUKTUR KOMPONEN YANG LAIN.

• LARUTAN PADAT BISA TERJADI SECARA SUBSITUSIONAL YAITU JIKA ATOM TERLARUT MENEMPATI POSISI ATOM PELARUT, ATAUPUN SECARA INTERSTISIAL YAITU JIKA ATOM TERLARUT MENEMPATI RUANG SELA ANTARA ATOM-ATOM PELARUT.

Page 8: Diagram Fasa Kel 4

ADA PERSYARATAN TERTENTU YANG HARUS DIPENUHI UNTUK MENCAPAI KEADAAN SATU FASA, YANG DIKENAL SEBAGAI KAIDAH HUME-ROTHERY, YAITU:

1. PERBEDAAN UKURAN ATOM PELARUT DAN ATOM TERLARUT KURANG DARI 15%.

2. STRUKTUR KRISTAL DARI KOMPONEN TERLARUT SAMA DENGAN KOMPONEN PELARUT.

Larutan Padat

Page 9: Diagram Fasa Kel 4

3. ELEKTRON VALENSI ZAT TERLARUT DAN ZAT PELARUT TIDAK BERBEDA LEBIH DARI SATU.

4. ELEKTRONEGATIVITAS ZAT TERLARUT DAN PELARUT KURANG-LEBIH SAMA, AGAR TIDAK TERJADI SENYAWA SEHINGGA LARUTAN YANG TERJADI DAPAT BERUPA LARUTAN SATU FASA.JIKA KAIDAH HUME-ROTHERY TIDAK TERPENUHI, MAKA YANG TERJADI BISA BERUPA CAMPURAN ATAU FASA PERALIHAN YANG MEMILIKI SUSUNAN KRISTAL BERBEDA DARI SUSUNAN KRISTAL KEDUA KOMPONEN YANG MEMBENTUKNYA.

Larutan Padat

Page 10: Diagram Fasa Kel 4

DIAGRAM BINER

Page 11: Diagram Fasa Kel 4

SISTEM BINER DENGAN KELARUTAN SEMPURNA

Page 12: Diagram Fasa Kel 4

SISTEM KELARUTAN TERBATAS

PADA METALURGI FISIK, SELAIN SYSTEM BINER DENGAN KELARUTAN SEMPURNA DIKENAL JUGA SYSTEM BINER DENGAN KELARUTAN TERBATAS. PADATAN DENGAN DUA KOMPONEN YANG SALING MELARUTKAN SECARA SEMPURNA TIDAKLAH BANYAK. YANG UMUM TERJADI ADALAH LARUTAN PADAT DENGAN KELARUTAN MASING-MASING KOMPONEN SECARA TERBATAS.

Page 13: Diagram Fasa Kel 4

SYSTEM BINER DENGAN KELARUTAN TERBATAS DAPAT DINYATAKAN DALAM

DIAGRAM EUTECTIC BINER, DAN

DIAGRAN PERITECTIC BINER.

Sistem Kelarutan Terbatas

Page 14: Diagram Fasa Kel 4

Sistem Kelarutan Terbatas

Page 15: Diagram Fasa Kel 4

Sistem Kelarutan Terbatas

Page 16: Diagram Fasa Kel 4

PEMBEKUAN DAN SEGREGASI• SOLIDIFIKASI ADALAH PROSES PEMBEKUAN

MATERIAL,DIMANA TERJADI SERANGKAIAN PERUBAHAN BENTUK DAN FASA. • SOLIDIFIKASI BERTUJUAN UNTUK MEMPEROLEH SIFAT-

SIFAT TERTENTU DARI BAHAN MATERIAL TERSEBUT• SELAMA PEMBEKUAN ATOM-ATOM MENYUSUN DIRINYA

SECARA TERATUR DAN BERULANG ULANG DENGAN GAYA IKATAN YANG KUAT MEMBENTUK LOGAM PADAT.

Page 17: Diagram Fasa Kel 4
Page 18: Diagram Fasa Kel 4

A). DIAGRAM CONTINUOUS COOLING TRANSFORMATION (CCT)UNTUK MENGGAMBARKAN LAJU PENDINGINAN YANG TIDAK DALAM KONDISI KESEIMBANGAN PENGARUH KECEPATAN PENDINGINAN MANERUS TERHADAP STRUKTUR MIKRO YANG TERBENTUK DAPAT DILIHAT DARI DIAGRAM INI

a

cb

Page 19: Diagram Fasa Kel 4

B). DIAGRAM TIME TEMPERATUR TRANSFORMATION (TTT)

Page 20: Diagram Fasa Kel 4

• JIKA PENDINGINAN TERJADI LEBIH CEPAT MAKA TERJADI SEGREGASI YAITU DISTRIBUSI YANG TIDAK MERATA YANG TERJADI DI DALAM BUTIR. PADA PUSAT BUTIR YANG PERTAMA MAMBEKU AKAN KAYA OLEH BAHAN YANG MEMPUNYAI TITIK LELEH TINGGI, BAHAN YANG MEMPUNYAI TITIK LELEH RENDAH AKAN NAIK MANJAUHI PUSAT BUTIR• FENOMENA INI DISEBUT “ CORED STRUCTURE• KELEMAHAN “CORED STRUCTURE” :• Ø  JIKA DIPADATKAN, AKAN CEPAT MELELEH.• Ø  MENGURANGI KEKUATAN MEKANIK PADA TEMPERATUR

TINGGI.

Page 21: Diagram Fasa Kel 4

REAKSI PERITEKTIKSISTEM EUTEKTIK SERING DIJUMPAI BILA TITIK CAIR DARI KEDUA KOMPONEN HAMPIR SAMA. TIPE KEDUA YANG PENTING PADA KONDISI TIGA FASA INVARIAN, YAITU REAKSI PERITEKTIK, ADALAH SISTEM DENGAN TITIK CAIR YANG SANGAT BERBEDA. BIASANYA REAKSI PERITEKTIK TERDAPAT PADA SISTEM YANG LEBIH RUMIT; SEPERTI SISTEM CU-ZN DENGAN RENTETAN TERDIRI DARI LIMA REAKSI PERITEKTIK.

Page 22: Diagram Fasa Kel 4

LARUT SEMPURNA DALAM KEADAAN CAIR, LARUT SEBAGIAN DALAM KEADAAN PADAT (REAKSI PERITEKTIK)

DIAGRAM FASA AG-PT MERUPAKAN CONTOH TERBAIK YANG MEMILIKI REAKSI PERITEKTIK.PADA SISTEM INI REAKSI PERITEKTIK, L + TERJADI PADA 42,4% AG DAN T= 1186C.

Page 23: Diagram Fasa Kel 4

REAKSI PERITEKTOID

REAKSI PERITEKTOID ADALAH REAKSI ISOTERMAL BOLAK BALIK (REVERSIBLE) ANTARA LOGAM BENTUK PADAT DAN LOGAM BENTUK PADAT LAINNYA PADA PROSES PENDINGINAN PADUAN LOGAM UNTUK MENGHASILKAN LOGAM BENTUK PADAT YANG BARU.

Page 24: Diagram Fasa Kel 4

REAKSI-REAKSI FASA YANG UMUM TERJADI