DEFINISI
KOROSI ADALAH KERUSAKAN ATAU DEGRADASI LOGAM AKIBAT REAKSI
REDOKS ANTARA SUATU LOGAM DENGAN BERBAGAI ZAT DI LINGKUNGANNYAYANG MENGHASILKAN SENYAWA-SENYAWA YANG TIDAK DIKEHENDAKI.
DALAM BAHASA SEHARI-HARI, KOROSI DISEBUT PERKARATAN
KOROSI ADALAH KEBALIKAN DARI PROSES EKSTRAKSI LOGAM DARI BIJIH
MINERALNYA
8/10/2019 KOROSI2.pdf
3/24
PROCESS
8/10/2019 KOROSI2.pdf
4/24
KOROSI BESI
8/10/2019 KOROSI2.pdf
5/24
PENGARUH PH
8/10/2019 KOROSI2.pdf
6/24
SEBAB KOROSI
KARENA LINGKUNGAN YANG KOROSIF
CACAT PADA BAHAN
8/10/2019 KOROSI2.pdf
7/24
REAKSI REDOX
OKSI SI : KEHILANGAN ELEKTRON (KENAIKAN BILANGAN OKSIDASI)
RE UKSI : PENAMBAHAN ELEKTRON (PENURUNAN BILANGAN OKSIDASI)
8/10/2019 KOROSI2.pdf
8/24
SEL GALVANIS ZN- CU
Katoda : menyerap elektron
Anoda : menghasilkan
elektron (terkorosi)
8/10/2019 KOROSI2.pdf
9/24
REDOX CU - ZN
BILA KONTAK DIHUBUNGKAN, SENG DAN
TEMBAGA AKAN TERHUBUNG, SEHINGGA
SENG AKAN MENJADI ANODA
(TERKOROSI) SEDANGKAN TEMBAGA
AKAN MENJADI KATODA (DILAPIS).
BILA KONTAK DIPUTUS, AKAN TERJADIPERBEDAAN TEGANGAN 1,1 VOLT
8/10/2019 KOROSI2.pdf
10/24
MACAMMACAM KOROSI
KOROSI LOGAM TAK SEJENIS (SEL KOMPOSISI)
SERANGAN KOROSI SECARA SELEKTIF (SEL TEGANGAN)
KOROSI CELAH DAN KOROSI SUMURAN (SEL KONSENTRASI)
KOROSI EROSI
RETAK PADA LOGAM (FATIGUE, KOROSI TEGANGAN
(INTERGRANULAR)
KOROSI PADA TEMPERATUR TINGGI
8/10/2019 KOROSI2.pdf
11/24
SEL KOMPOSISI TERBENTUK APABILA ADA 2 LOGAM BERLAINAN JENIS SALING TERHUBUNG SATU
SAMA LAIN
8/10/2019 KOROSI2.pdf
12/24
SEL TEGANGAN
TERBENTUK PADA BATAS BUTIR YANG TERKOROSI (DIETSA), ATOM-ATOM
PADA BATAS ANTAR BUTIR MEMPUNYAI POTENSIAL ELEKTRODA YANG
BERBEDA DARI ATOM-ATOM DALAM BUTIR. MAKA TERJADILAH ANODA
KATODA. DAERAH BATAS BUTIR DAPAT DIANGGAP BERTEGANGAN, KARENA
ATOM-ATOM TIDAK BERADA PADA KONDISI ENERGI YANG TERENDAH.
PENGERJAAN DINGIN DAPAT MEMBAWA PENGERUH BURUK YAITU
MENIMBULKAN KOROSI YANG DITIMBULKAN OLEH PENGERASAN-REGANG.
8/10/2019 KOROSI2.pdf
13/24
SEL TEGANGAN
8/10/2019 KOROSI2.pdf
14/24
SEL KONSENTRASI
SEL KONSENTRASI MEMPERCEPAT KOROSI DI DAERAH DIMANA KONSENTRASI
ELEKTROLIT LEBIH RENDAH, MISALNYA OKSIGEN YANG TERDAPAT DI UDARA
APABILA BERSENTUHAN DENGAN PERMUKAAN LOGAM YANG LEMBAB, KOROSI
AKAN TERJADI PADA DAERAH YANG KONSENTRASI OKSIGENNYA KECIL
(KEKURANGAN OKSIGEN)
8/10/2019 KOROSI2.pdf
15/24
PENCEGAHAN KOROSI
PELAPISAN LOGAM, TERUTAMA UNTUK MATERIAL YANG MEMPUNYAI
POTENSIAL YANG LEBIH TINGGI
BILA MENGGUNAKAN BEBERAPA MACAM LOGAM, MAKA HARUS DIHINDARI
KONTAK ANTAR LOGAM TERSEBUT
MENGGUNAKAN MATERIAL YANG YANG MEMPUNYAI POTENSIAL YANG HAMPIR
SAMA
8/10/2019 KOROSI2.pdf
16/24
PASSIVATION
MEMBUAT MATERIAL MENJADI KURANG REAKTIF TERHADAP LINGKUNGAN
ADA LOGAM YANG MEMPUNYAI LAPISAN OKSIDA ALAMI YANG MELINDUNGI DARIKOROSI LEBIH LANJUT, MISAL ALUMINIUM
8/10/2019 KOROSI2.pdf
17/24
ANODIZING
PEMBENTUKAN LAPISAN FILM DENGAN MENGGUNAKAN ELEKTROLIT PADA LOGAM
YANG MENJADI ANODA.
8/10/2019 KOROSI2.pdf
18/24
UJI KOROSI
DENGAN PENGUJIAN LANGSUNG KE PENGGUNA
DENGAN SAMPEL MATERIAL
MEMPERCEPAT REAKSI
8/10/2019 KOROSI2.pdf
19/24
8/10/2019 KOROSI2.pdf
20/24
DEFINISI
MATERIALYANG TERBUAT DARI DUA BAHAN ATAU LEBIH YANG TETAP
TERPISAH DAN BERBEDA DALAM LEVEL MAKROSKOPIK SELAGI MEMBENTUK
KOMPONEN TUNGGAL.
http://id.wikipedia.org/wiki/Materialhttp://id.wikipedia.org/wiki/Materialhttp://id.wikipedia.org/wiki/Material8/10/2019 KOROSI2.pdf
21/24
KEUNTUNGAN
DARI 2 MATERIAL YANG BERBEDA, DAPAT DIGABUNGKAN MENJADI SATU
MATERIAL DENGAN SIFAT YANG BARU
8/10/2019 KOROSI2.pdf
22/24
MATRIX & REINFORCEMENT
REINFORCEMENT : PENGUAT
MATRIX : PENGISI/PEMBUNGKUS UNTUK MENJAGA BENTUK
8/10/2019 KOROSI2.pdf
23/24
8/10/2019 KOROSI2.pdf
24/24