Tugas XRD 1
Interpretasikan pola XRD hidrotalsit berikut meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
XRD patterns of hydrotalcite with interlayer carbonate synthesized at 423 K (HT423as); after calcination at 723 K (HT423calc); after calcination/rehydration (HT423rehydr); hydrotalcite with interlayer oxalate (HTox) and HTox after ion exchange with KOH (HTex). indicates superlattice reflection.
Journal of Catalysis 203, 184191 (2001)
-
Tugas XRD - 2
Interpretasikan pola XRD lempung terpilar silika-besi oksida termodifikasi template organik (DS-distearil dimetilammonium klorida, MS-trimetil stearilammonium klorida, OD-oktadesil ammonium klorida) meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
X-Ray diffraction profiles of the pristine SFM (SiO2Fe2O3 sol pillared montmorillonite) (a) and the organically modified samples obtained after calcining at 550 C for among the organic templates used. This implies that the 2 h; (b) SFM-OD, (c) SFM-MS and (d) SFM-DS, respectively
J. Mater. Chem., 1998, 8(6), 14591463
-
Tugas XRD - 3
Interpretasikan pola XRD lempung terpilar TiO2 termodifikasi template organik meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
Powder XRD patterns of MNT, C1, C8, C12 and C18TMAMNT, compared with MNT calcined at 823 K and anatase powder (PT-2); peaks marked are unidentified.
J . M a t e r . C h e m . , 2 0 0 4 , 1 4 , 2 7 6 3 2 7 6
-
Tugas XRD - 4
Interpretasikan pola XRD MCM-41 meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
Powder X-ray diffraction patterns of MCM-41 samples. Silica content in bracket
Langmuir 1996, 12, 6513-6517
-
Tugas XRD - 5
Interpretasikan pola XRD mesopori titania meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
Powder X-ray diffraction patterns of the as-made Na+-free titania followed by hydrothermal treatment in TMAOH solution, pH ) 11.5 (50 mL of TMAOH solution/g of sample) at 100 C for (a) 0 day (as-made sample), (b) 7 days and (c) 14 days.
Powder X-ray diffraction patterns of as-made Na+-free titania followed by hydrothermal treatment in NaOH solution, pH ) 11.5 (50 mL of NaOH solution/g of sample) at 100 C for (a) 0 day (as-made sample), (b) 7 days and (c) 14 days.
Langmuir 1999, 15, 8561-8564
-
Tugas XRD - 6
Interpretasikan pola XRD film mesopori titania meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
X-Ray diffraction diagrams for 350 oC treated F127-templated TiO2 films previously aged following (a) conditions 1 and (b) conditions 2. A 1 day old film (at room temperature and RH = 50%) F127-templated TiO2 film (Conditions 1) treated at 350 oC A 2 week old film (at room temperature and RH = 50%), heated at 60 oC for 24 hours followed by 130 oC for 24 hours (Conditions 2), and finally calcined at 350 oC
New J. Chem., 2003, 27, 913
-
Tugas XRD - 7
Interpretasikan pola XRD material silika SBA-15 meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
XRD pattern of SBA-15 synthesized at 60, 100 and 130 oC and calcined at 550 oC
New J. Chem., 2003, 27, 7379
-
Tugas XRD - 8
Interpretasikan pola XRD lempung terpilar TiO2 termodifikasi template organik meliputi pengindeksan (penentuan dhkl : dengan teknik spectra matching) dan makna pergeseran dhkl
Effect of TiP/scCO2 treatment time on the powder XRD patterns of (a) MNT, (b) C1TMAMNT and (c) C18TMAMNT. (scCO2 = supercritical CO2)
J . M a t e r . C h e m . , 2 0 0 4 , 1 4 , 2 7 6 3 2 7 6