PTR-5028 ASTM B117 Salt Spray Test of Swagelok 8GB and ...

Product Test Report

PTR-5028 Swagelok Company Ver 00 29495 F.A. Lennon Dr. September 2020 Solon, Ohio 44139 U.S.A. of 6

2020 Swagelok Company

TITLE ASTM B117 Salt Spray Test of Swagelok® 8GB and 16GB Series General Service Ball Valves, Tested by Element Materials Technology PRODUCT TESTED

Series Example Ordering Numbers Quantity

8GB SS-8GBF6 2

16GB SS-16GBF16 2

PURPOSE This test was performed under laboratory conditions to observe the effects of extended salt spray exposure on valve materials and valve performance. TEST CONDITIONS Salt Spray

• Performed by Element Materials Technology • Media: 5% salt solution • Temperature: 95°F (35°C) • Duration: 672 hours

Performance

• Performed by Swagelok • Pressure: 80 psig (5.5 bar), 1000 psig (68.9 bar), and 6000 psig (413 bar) • Test temperature: 70°F (20°C) • Media: nitrogen • Seat test: max allowable leak rate 0.1 std cm3/min. • Shell test: no detectable leakage with liquid leak detector

TEST METHOD Salt Spray: The test procedure was in accordance with ASTM-B117-19. Performance: After salt spray testing, all valves were performance tested in both directions with nitrogen. TEST RESULTS The third-party lab test report observations are included at the end of this product test report. The following images show the valve surface appearance during the salt spray procedure. All valves passed subsequent performance testing to the above-stated performance criteria.

Product Test Report



Test Results for SS-8GBF6

Time Results

24 hours No visible change.





504 hours Light corrosion forming on the outside body and end screws

was observed.

672 hours

Evidence of isolated spots of red rust corrosion was visible

on both samples. The total corrosion was

estimated at less than 5% of the total surface area of each part.

Product Test Report



SS-8GBF6 Valve 1 Discoloration

Before Test After Test



Product Test Report



Test Results for SS-16GBF16

Time Results






504 hours Light corrosion forming on the

outside body and end screws was observed.

672 hours

Evidence of isolated spots of red rust corrosion was visible on both

samples. The total corrosion was estimated at less than 5 to 10% of the total

surface area of each part.

Product Test Report






Before Test After test

Product Test Report



These tests were performed to consider a specific set of conditions and should not be considered valid outside those conditions. Swagelok Company makes no representation or warranties regarding these selected conditions or the results attained. Laboratory tests cannot duplicate the variety of actual operating conditions. Test results are not offered as statistically significant. See the product catalog for technical data. SAFE PRODUCT SELECTION When selecting a product, the total system design must be considered to ensure safe, trouble-free performance. Function, material compatibility, adequate ratings, proper installation, operation, and maintenance are the responsibilities of the system designer and user. Referenced Documents ASTM B 117: 2019, Standard Practice for Operating Salt Spray (fog) apparatus, ASTM- American Society Testing & Materials, 100 Barr Harbor Drive P.O. Box C700 West Conshohocken, PA 19428-2959, USA, www.astm.org

Swagelok—TM Swagelok Company

Contact: Ralph Lucarelli Swagelok Co. 318 Bishop Rd Highland Hts, OH 44143

TEST REPORT — EAR-CONTROLLED DATA Date: 7/15/2020 P.O. No.: 4503729080 W/O No.: CRA002-20-06-31622-1 Date Received: 6/10/2020

The above testing was performed in accordance with the latest revision of the applicable commercial, military and/or International test method unless otherwise noted. The above services were performed in accordance with Element Materials Technology Cleveland’s Quality Manual, Edition 1, Revision 5, dated August 16, 2012. Information and statements in this report are derived from material, information and/or specifications furnished by the client and exclude any expressed or implied warranties as to the fitness of the material tested or analyzed for any particular purpose or use. This laboratory does not perform sampling as sampling is done by the customer. The results of all tests reported apply only to the sample material(s) received and tested. This report is the confidential property of our client and may not be used for advertising purposes. This report shall not be reproduced except in full, without written approval of this laboratory. The recording of false, fictitious or fraudulent statements or entries on this document may be punished as a felony under Federal Statutes. Sample remnants are held for a minimum of 6 months following issuance of test results, at which point they will be discarded unless notified in writing by the client. This material was not contaminated by mercury or chlorinated solvents during the handling and processing at Element Materials Technology Cleveland.

Tammy Storm Administrative Manager

Page 1 of 1

Sample Description: Two (2) Valve Assemblies, P/N: CO2-SS-8GBF6 SALT SPRAY TESTING PER ASTM B117 Outside testing services were performed at a sub-contracted laboratory that has been audited and approved by Element Materials Technology Cleveland. Please refer to their test report for their analysis and conclusions. Laboratory Name: Element Newtown

Test Report #: HER023-06-12-91452-1 This document contains technical data whose export and re-export/retransfer is subject to control by the U.S. Department of Commerce under the Export Administration Act and the Export Administration Regulations. The Department of Commerce’s prior written approval may be required for the export or re-export/retransfer of such technical data to any foreign person, foreign entity or foreign organization whether in the United States or abroad.

Contact: Karen Meadows Element Cleveland 5405 E. Schaaf Road CLEVELAND, OH 44131

TEST CERTIFICATE — EAR-CONTROLLED DATA

Date: 7/14/2020 P.O. No.: ECL022272PO-1 W/O No.: HER023-06-12-91452-1

Respectfully submitted

Francine Dwyer Quality Administrator

Information and statements in this report are derived from material, information and/or specifications furnished by the client and exclude any expressed or implied warranties as to the fitness of the material tested or analyzed for any particular purpose or use. The testing reported on this certification has been performed in accordance with QSM 5th Edition, Rev. 0, Effective 3/15/2020 and related procedures. All testing has been performed in accordance with the latest revision of the applicable published test method in effect at the time of testing, unless otherwise stated. Measurement uncertainty was not considered when making statements of conformity to a specification or standard, unless otherwise specified. This report shall not be reproduced except in full, without written approval of this laboratory. The recording of false, fictitious, or fraudulent statements or entries on this document may be punished as a felony under Federal Statutes including Federal Law Title 18, Chapter 47. Sample remnants are held for a minimum of 30 days following issuance of test results, at which point they will be discarded unless notified in writing by the client.

ALL TESTING PERFORMED IN A MERCURY-FREE ENVIRONMENT Page 1 of 10

PART NUMBER CO2-SS-8GBF6 WO# CRA002-20-06-31622-1 DESCRIPTION Valve Assemblies SPECIFICATION ASTM-B117-19 / Customer Info / Customer Requirement

Salt Spray Results Requirements: ASTM-B117-19 / Customer Info / Customer Requirement

2 samples supported or suspended between 15° and 30 ° were tested in a salt chamber using a 5% salt sol ution at 95oF for a total of 672 hours, tested in accordance with ASTM-B117-19. Time Results 24 Hours No visible Change. 72 Hours No visible Change. 192 Hours No visible Change. 336 Hours No visible Change. 384 Hours No visible Change. 504 Hours Observation of light Corrosion forming on the outside body and end Nuts. 672 Hours Visual evidence of isolated spots of Red Rust corrosion visible on both samples,

total corrosion estimated at less than 5% of total surface area of each part. All tests listed on this certification have been performed in accordance with ASTM-B117-19 / Customer Info / Customer Requirement and the tested samples do conform to the requirements. This document contains technical data whose export and re-export/ retransfer is subject to control by the U.S. Department of Commerce under the Export Administration Act and the Export Administration Regulations. The Department of Commerce’s prior written approval may be required for the export or re-export/retransfer of such technical data to any foreign person, foreign entity or foreign organization whether in the United States or abroad.








72 Hours








144 Hours








192 Hours








336 Hours








384 Hours (Before Holiday Weekend)








504 Hours








672 Hours (Completion of Testing). 3 Photos

Contact: Ralph Lucarelli Swagelok Co. 318 Bishop Rd Highland Hts, OH 44143

TEST REPORT — EAR-CONTROLLED DATA Date: 7/15/2020 P.O. No.: 4503729080 W/O No.: CRA002-20-06-31622-2 Date Received: 6/10/2020

The above testing was performed in accordance with the latest revision of the applicable commercial, military and/or International test method unless otherwise noted. The above services were performed in accordance with Element Materials Technology Cleveland’s Quality Manual, Edition 1, Revision 5, dated August 16, 2012. Information and statements in this report are derived from material, information and/or specifications furnished by the client and exclude any expressed or implied warranties as to the fitness of the material tested or analyzed for any particular purpose or use. This laboratory does not perform sampling as sampling is done by the customer. The results of all tests reported apply only to the sample material(s) received and tested. This report is the confidential property of our client and may not be used for advertising purposes. This report shall not be reproduced except in full, without written approval of this laboratory. The recording of false, fictitious or fraudulent statements or entries on this document may be punished as a felony under Federal Statutes. Sample remnants are held for a minimum of 6 months following issuance of test results, at which point they will be discarded unless notified in writing by the client. This material was not contaminated by mercury or chlorinated solvents during the handling and processing at Element Materials Technology Cleveland.

Tammy Storm Administrative Manager

Page 1 of 1

Sample Description: Two (2) Valve Assemblies, P/N: CO2-SS-16GBF16 SALT SPRAY TESTING PER ASTM B117 Outside testing services were performed at a sub-contracted laboratory that has been audited and approved by Element Materials Technology Cleveland. Please refer to their test report for their analysis and conclusions. Laboratory Name: Element Newtown

Test Report #: HER023-06-12-91452-2 This document contains technical data whose export and re-export/retransfer is subject to control by the U.S. Department of Commerce under the Export Administration Act and the Export Administration Regulations. The Department of Commerce’s prior written approval may be required for the export or re-export/retransfer of such technical data to any foreign person, foreign entity or foreign organization whether in the United States or abroad.








PART NUMBER CO2-SS-16GBF16 WO# CRA002-20-06-31622-2 DESCRIPTION Valve Assemblies SPECIFICATION ASTM-B117-19 / Customer Info / Customer Requirement

Salt Spray Results Requirements: ASTM-B117-19 / Customer Info / Customer Requirement

2 samples supported or suspended between 15° and 30 ° were tested in a salt chamber using a 5% salt sol ution at 95oF for a total of 672 hours, tested in accordance with ASTM-B117-19. Time Results 24 Hours No visible Change. 72 Hours No visible Change. 192 Hours No visible Change. 336 Hours No visible Change. 384 Hours No visible Change. 504 Hours Observation of light Corrosion forming on the outside body and end Nuts. 672 Hours Inspection Visual evidence of isolated spots of Red Rust corrosion visible on both samples,

total corrosion estimated at 5%-10% of total surface area of each part.

All tests listed on this certification have been performed in accordance with ASTM-B117-19 / Customer Info / Customer Requirement and the tested samples do conform to the requirements. This document contains technical data whose export and re-export/ retransfer is subject to control by the U.S. Department of Commerce under the Export Administration Act and the Export Administration Regulations. The Department of Commerce’s prior written approval may be required for the export or re-export/retransfer of such technical data to any foreign person, foreign entity or foreign organization whether in the United States or abroad.