PENGARUH KOROSI LINGKUNGAN PANTAI PADA ALUMINIUM PADUAN .PADA ALUMINIUM PADUAN 8,5% SILIKON 4%...

download PENGARUH KOROSI LINGKUNGAN PANTAI PADA ALUMINIUM PADUAN .PADA ALUMINIUM PADUAN 8,5% SILIKON 4% TEMBAGA.

If you can't read please download the document

  • date post

    10-Mar-2019
  • Category

    Documents

  • view

    214
  • download

    0

Embed Size (px)

Transcript of PENGARUH KOROSI LINGKUNGAN PANTAI PADA ALUMINIUM PADUAN .PADA ALUMINIUM PADUAN 8,5% SILIKON 4%...

i

PENGARUH KOROSI LINGKUNGAN PANTAI

PADA ALUMINIUM PADUAN 8,5% SILIKON 4% TEMBAGA

SKRIPSI

Untuk memenuhi sebagian persyaratan

mencapai derajat sarjana S-1

Diajukan oleh:

RADITYA OMEGAWAN SAMBODO

NIM: 125214032

PROGRAM STUDI TEKNIK MESIN

JURUSAN TEKNIK MESIN

FAKULTAS SAINS DAN TEKNOLOGI

UNIVERSITAS SANATA DHARMA

YOGYAKARTA

2016

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

ii

THE CORROSION OF ALUMINIUM ALLOY 8,5% SILICON 4% COPPER

IN TROPICAL COASTAL ATMOSPHERES

FINAL PROJECT

As partial fulfillment of the requirement

to obtain the Sarjana Teknik Degree

in Mechanical Engineering

by

RADITYA OMEGAWAN SAMBODO

Student Number: 125214032

MECHANICAL ENGINEERING STUDY PROGRAM

MECHANICAL ENGINEERING DEPARTMENT

FACULTY OF SCIENCE AND TECHNOLOGY

SANATA DHARMA UNIVERSITY

YOGYAKARTA

2016

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

PENGARUH KOROSI LINGKUNGAN PANTAI

PADA ALUMINIUM PADUAN 8,5% SILIKON 4% TEMBAGA

Disusun oleh

Nama: Raditya Omegawan Sambodo

NIM: 125214032

Telah Disetujui Oleh:

Yogyakarta, 16 Juni 2016

Pembimbing Utama

Bud etyahandana, S.T., M)'.

iii

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

v

PERNYATAAN

Dengan ini saya menyatakan bahwa dalam skripsi ini tidak terdapat karya yang

pernah diajukan untuk memperoleh gelae kesarjanaan di suatu perguruan tinggi,

dan sepanjang pengetahuan saya juga tidak terdapat karya atau pendapat yang

ernah ditulis atau diterbitkan oleh orang lain, keculai secara tertulis diacu dalam

naskah ini dan disebutkan dalam daftar pustaka.

Yogyakarta, 16 Juni 2016

Raditya Omegawan Sambodo

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

vi

INTISARI

Pada penelitian ini penulis tergerak untuk meneliti material yang cocok untuk digunakan sebagai sudu kincir angin yang terdapat pada lingkungan pantai.

Dikarenakan peneliti tertarik saat membaca salah satu berita, mengatakan

peningkatan penggunaan listrik dan pemerintah akan mengadakan proyek

pembangkit listrik 35.000 megawatt. Alternatif logam paduang yang dipilih

adalah Al-Si-Cu yang masing masing logam mempunyai tujuannya masing

masing. Aluminium memiliki sifat yang ringan mudah dibentuk, dan silicon

memiliki sifat yang tahan korosi sedangkan sifat dari tembaga adalah ulet. Tujuan

dari penelitian ini untuk mengetahui pengaruh penambahan 8,5Si dan 4%Cu pada

massa jenis, perubahan massa dan kekuatan tarik aluminium.

Proses pengecoran dari aluminium kondisi awal dan aluminium paduan

8,5%Si dan 4%Cu sebagai mengawali penelitian. Seletah proses pengecoran

selesai logam ini mengalami proses pembentukan spesimen. Spesimen yang

dibentuk untuk pengujian kekuatan tarik menurut standar ASTM A370, dengan

spesimen memiliki panjang ukur 25 mm dan diameter ukur 6,25 mm. setelah itu

spesimen ada yang tidak dikorosi atau 0 bulan ada yang dikorosi sampai 4 bulan.

Pengkorosian dilakukan di pinggir Pantai Pelangi, Bantul, Yogyakarta. Dan setiap

bulanya tiga spesimen diambil untuk di catat perubahan massa dan diujian

kekuatan tarik

Pengaruh penambahan 8,5%Si-4%Cu meningkatnya massa jenis sebesar 4% dari spesimen aluminium kondisi awal, yang awalnya 2674,59 gr/dm

3 menjadi

2782,50 gr/dm3. Pada kekuatan tarik spesimen paduan Al-8,5%Si-4%Cu

meningkat 32% dari spesimen aluminium kondisi awal. Rata-rata penurunan

kekuatan tarik aluminium kondisi awal adalah 21,25 Mpa per bulannya dan

penurunan kekuatan tarik spesimen paduan 3,90 Mpa per bulannya. Spesimen

aluminium kondisi awal setelah diberikan perlakuan korosi selama empat bulan

menyebabkan penurunan kekuatan tarik. Penurunannya sebesar 75,42%, sehingga

pada bulan keempat menjadi 27,67 Mpa yang awalnya sebesar 112,71Mpa.

Setelah diberikan pembahan 8%Si dan 4%Cu pada spesimen aluminium,

memberikan hasil yang lebih baik pada nilai kekuatan tariknya. penurunannya

sebesar 13% dengan bulan keempat 117,28 Mpa dan awal sebelum diberi

perlakuan korosi 135,39 Mpa.

Kata kunci: aluminium, massa jenis, kekuatan tarik.

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

vii

ABSTRACT

In this research, the researcher move to examine the suitable material

which would be used to as a propeller of windwill where is placed on the coastal

environment. There is news which had already read by the researcher. It is said

that there are the increased use of the electricity therefore the government would

hold power plant project 35.000 megawatts. The alloy of the alternatif metal

which is chosen is AL Si-Cu. Each metal have different characteristics.

Aluminium have character which it is light and easy to be transformed. The

silicon have a corrosion resistant properties. Then the nature of Copper is resilent.

The purpose of this reseach is to know the influence of the addition 8,5 % Si and

4% Cu on the density, the changing of massa, and the tensile strength of

Aluminium

The process of the casting from the initial condition Aluminium and

Aluminium alloy 8,5%Si and 4%Cu started the research. After the process of

casting is done, these metals were transformed into specimen. This specimen was

formed to test the tensile strength according to standard of ASTM A370. This

specimen have measurement that is 25mm in length and 6,25 mm in diameter.

Then both of them got treatment, one specimen is not corroded or nol month and

the other was corroded during four mounth. The corrosion had done on the shore

of the Rainbow, Bantul, Yogyakarta. Every months, there are three specimen was

taken in order to note the changing of density and tensile strength.

The influence of the addition 8,5 % Si and 4%Cu to Aluminium produces

the density increased by 4% from the initial condition of Aluminium. It was

originally 2674,59 gr/dm3 into 2782,50 gr/dm

3.The tensile strength of specimen is

the alloy Al-8,5%Si-4%Cu had increased 32% from the initial condotion of

Aluminium. The average decreased of the tensile strength of the initial condition

was 21,25 Mpa per month and the decreased of the tensile strength of specimen

3,90 Mpa per month. The initial condition of specimen aluminium after was

given the corrotion of treatment during four month cause the decreased of tensile

strength. The decresed is amount 75,42% therefore the initial condition which is

112,71Mpa becomes 27,67Mpa during four month. After the treatment was given

which is addition 8,5%Si and 4%Cu on the specimen Aluminium, the result was

better on the tensil strength. The decreased was amount 13% which the inital

condition 135,39 Mpa became 117,28 Mpa on the fourth month..

Keywords: aluminium, density, the tensil strength

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

viii

LEMBAR PERNYATAAN PERSETUJUAN

PUBLIKASI KARYA ILMIAH UNTUK KEPENTINGAN

AKADEMIS

Yang bertanda tangan di bawah ini, saya mahasiswa Universitas Sanata Dharma

Yogyakarta:

Nama : Raditya Omegawan Sambodo

NIM : 125214032

Dengan pengembangan ilmu pengetahuan, saya memberikan kepada Perpustakaan

Universitas Sanata Dharma Yogyakarta skripsi saya yang berjudul:

PENGARUH KOROSI LINGKUNGAN PANTAI PADA AL

8,5%SI 4%CU

Dengan demikian saya memberikan kepada Perpustakaan Universitas Sanata

Dharma Yogyakarta hak untuk menyimpan, mengalihkan dalam bentuk media

lain, mengelolanya di internet atau media lain untuk kepentingan akademis tanpa

perlu meminta ijin dari saya maupun memberikan royalty kepada saya selama

tetap mencantumkan nama saya sebagai penulis.

Demikian pernyataan ini saya buat dengan sebenarnya.

Dibuat di Yogyakarta

Pada tanggal: 16 Juni 2016

Yang menyatakan,

(Raditya Omegawan Sambodo)

PLAGIAT MERUPAKAN TINDAKAN TIDAK TERPUJI

ix

KATA PENGANTAR

Puji Syukur kehadirat Tuhan Yang Maha Esa yang selalu mencurahkan

berkat dan karunia-Nya sehingga penulis dapat menyelesaikan skripsi ini yang

berjudul Pengaruh Korosi Lingkungan Pantai pada Aluminium Padua 8,5%Cu

4%Si dengan baik dan lancar. Penulisan skripsi ini memiliki tujuan untuk

memenuhi syarat dalam mencapai gelar Sarjana Teknik Jurusan Teknik Mesin

Fakultas Saint dan Teknologi Santa dharma Yogyakarta.

Dalam proses skripsi ini penulis menyadari adanya keterbatasan yang

dimiliki. Akan tetapi berkat bimbingan dan dukungan yang diberikan oleh

berbagai pihak akhirnya penulis dapat menyelesaikan skripsi ini. Oleh karenanya,

penulis mengucapkan terima kasih kepada:

1. Rektor

2. Sudi Mungkasi, PhD, Dekan Fakultas Sains dan Teknologi Universitas

Sanata Dharma Yogyakarta.

3. Ir. Petrus Kanisius Purwadi, S.T., M.T., Ketua Program Studi Teknik Mesin

Universitas Sanata Dharma Yogyakarta.

4. Budi Setyahandana, S.T., M.T., selaku dosen pembimbing, terimakasih untuk

bimbingan serta paradigma yang dicontohkan selama i