7/23/2019 PROSES MANUFAKTUR 7
1/21
EXTRUSIONDEPARTEMEN TEKNIK INDUSTRIUNIVERSITAS SUMATERA UTARA
7/23/2019 PROSES MANUFAKTUR 7
2/21
EXTRUSION ADALAH PROSES PENEKANANBILLET BERBENTUK SILINDER SEHINGGAMELEWATI/MELALUI CETAKAN DANBENTUKNYA AKAN MENGIKUTI CETAKAN
SELAMA PROSES EXTRUSION MATERIALMENGALAMI GAYA KOMPRES/TEKAN TRIAXIAL,MATERIAL MENGALAMI DEFORMASI YANGBESAR TANPA FRACTURE
BEBERAPA PRODUK TERCIPTA MELALUIPROSES INI REL PINTU SORONG, RANGKA
JENDELA, GEAR, HANGERS DAN SEBAGAINYA.
ALUMUNIUM, COPPER, STEEL DANMAGNESIUM ADALAH MATERIAL YANG SERING
INTRODUCTION
7/23/2019 PROSES MANUFAKTUR 7
3/21
7/23/2019 PROSES MANUFAKTUR 7
4/21
CONTOH PRODUK
EXTRUSION
7/23/2019 PROSES MANUFAKTUR 7
5/21
PROSES EXTRUSI BERGANTUNG KEPADATINGKAT DUCTILITY MATERIAL EXTRUSI DAPAT DILAKUKAN PADA
TEMPERATUR RUANG DAN TEMPERATURTINGGI DRAWING ADALAH PROSES PENGURANGAN
LUAS AREA ATAU PEMBENTUKAN WIRE,
TUBING, SOLID ROD DENGAN MENARIKMELALUI CETAKAN.
INTRODUCTION
7/23/2019 PROSES MANUFAKTUR 7
6/21
ADA TIGA TIPE PROSES EXTRUSI YAITU DIRECT EXTRUSI DIMANA PENEMPATAN BILLET
DIDALAM CHAMBER/CONTAINER DANKEMUDIAN DITEKAN OLEH HYDRAULIK AM
HINGGA BILLET MELALUI CETAKAN. INDIRECT EXTRUSI (REVERSE, BACKWARD)
DIMANA CETAKAN BERGERAK SEPANJANGBILLET UNTUK MENGURANGI LUAS AREANYA.
LATERAL (SIDE) EXTRUSI DIMANA BILLETBERADA DALAM POSISI VERTIKAL DANMENDAPAT PENEKANAN DARI ATAS.
PROSES EXTRUSI
7/23/2019 PROSES MANUFAKTUR 7
7/21
PROSES EXTRUSI
7/23/2019 PROSES MANUFAKTUR 7
8/21
VARIABEL GEOMETRI DALAM PROSES EXTRUSIADALAH SUDUT CETAKAN DAN RASIO LUAS AREABILLET SEBELUM DAN SESUDAH DIEXTRUSI (R)
VARIABEL LAIN YANG MEMPENGARUHI PROSES
EXTRUSI ADALAH TEMPERATUR BILLET, KECEPATANHIDRAULIK RAM DAN LUBRICANT YANG DIGUNAKAN.
GAYA YANG DIBUTUHKAN DALAM PROSES EXTRUSIBERGANTUNG KEPADA STRENGTH BILLET, RASIOEXTRUSI DAN GESEKAN ANTARA BILLET DANCONTAINER DAN BILLET DENGAN CETAKAN
F AO! L" (AO/ A#)
PROSES EXTRUSI
7/23/2019 PROSES MANUFAKTUR 7
9/21
PROSES EXTRUSI
7/23/2019 PROSES MANUFAKTUR 7
10/21
NILAK k
7/23/2019 PROSES MANUFAKTUR 7
11/21
SEBUAH BILLET TERBUAT DARI $%&'% BRASSDI EXTRUSI PADA TEMPERATUR $%%%C.DIAMETER BILLET ADALAH * ++ DANDIAMETER SETELAH EXTRUSI ADALAH *%++. HITUNGLAH GAYA YANG DIBUTUHKAN.
CONTOH PERHITUNGAN
7/23/2019 PROSES MANUFAKTUR 7
12/21
NILAI ! SETELAH MELIHAT GAMBAR ADALAH*% M- MAKA GAYA YANG DIBUTUHKANADALAH
F (*)/ 0 (*%) L" ((*) /(*%)) F *.1 MN
7/23/2019 PROSES MANUFAKTUR 7
13/21
METAL FLOW PADA PROSES EXTRUSI AKANMEMPENGARUHI KUALITAS DANMECHANICAL PROPERTI DARI PRODUKEXTRUSI.
POLA ALIRAN DIBENTUK SESUAI PRINSIPENERGY DIKURANGI DALAM SETIAP PROSES.
METAL FLOW MEMBENTUK LONGITUDINAL
SEHINGGA PRODUK EXTRUSI AKANMEMBENTUK PERPANJANGAN GRAINSTRUKTUR
STRUKTUR MATERIAL PADA
PROSES EXTRUSI
7/23/2019 PROSES MANUFAKTUR 7
14/21
7/23/2019 PROSES MANUFAKTUR 7
15/21
DALAM PRAKTEKNYA R BIASANYA ANTARA%&%%.
PANJANG PRODUK EXTRUSI BIASANYAKURANG DARI $.* +
KECEPATAN RAM 2 % SAMPAI DENGAN %.*+/3
SUDUT MATA CETAKAN DAPAT MEMBENTUK
SISA MATERIAL YANG TERTINGGAL DICHAMBER.
PROSES PARAMETER
7/23/2019 PROSES MANUFAKTUR 7
16/21
UNTUK METAL DAN ALLOY YANG TIDAK MEMILIKITINGKAT DUCTILITY YANG BAIK/CUKUP DALAMTEMPERATUR RUANG, MAKA PROSES EXTRUSIDILAKUKAN PADA TEMPERATUR TINGGI.
HOT EXTRUSI DAPAT MENYEBABKANKERUSAKAN PADA CETAKAN, PENDINGINANPERMUKAAN HOT BILLET DAN MENGHASILKANNON UNIFORM DEFORMATION
AKIBAT PEMANASAN PADA BILLET AKANMENIMBULKAN OXIDE FILM PADA PERMUKAANBILLET
HOT EXTRUSI
7/23/2019 PROSES MANUFAKTUR 7
17/21
S4UARE DESAIN DIGUNAKAN UNTUKMENGEXTRUSI NON FERROUS METAL TERUTAMAUNTUK ALUMUNIUM.
TUBING DIEXTRUSI DAN MEMBENTUK SOLID
ATAU BILLET YANG BERONGGA. DIMANAMANDREL AKAN LENGKET PADA HIDRAULIK RAM.
UNTUK MEMBENTUK RONGGA DAPATMENGGUNAKAN METODE WELDING CHAMBER
METHOD ATAU MENGGUNAKAN VARIASI CETAKANSEPERTI SPIDER DIE, PORTHOLE DIE DAN BRIDGEDIE.
DESAIN CETAKAN
7/23/2019 PROSES MANUFAKTUR 7
18/21
DESAIN CETAKAN
7/23/2019 PROSES MANUFAKTUR 7
19/21
DESAIN CETAKAN
7/23/2019 PROSES MANUFAKTUR 7
20/21
DESAIN CETAKAN
7/23/2019 PROSES MANUFAKTUR 7
21/21
MATERIAL UNTUK HOT EXTRUSI ADALAHHOT WOR DIE STEEL YANG DI COATINGDENGAN 5IRCONIA.
LUBRIKASI AKAN MEMBERIKAN EFEK KEPADAALIRAN MATERIAL, SURFACE FINISH,KUALITAS PRODUK DAN GAYA EXTRUSI.
GLASS ADALAH LUBRIKAN YANG COCOK
UNTUK STEEL, STAILEES STEEL DAN HIGHTEMPERATURE METAL.
MATERIAL CETAKAN DAN
LUBRIKASI