Aluminium and Aluminium Alloy
Sifat aluminium:• Ringan (berat jenis 2,7; ± ⅓ baja)• Lunak/ulet• Tahan korosi• Sifat penghantaran panas dan listrik tinggi• Non toxic, non magnetic, non sparking• Kekuatan dan kekakuan rendah• Mudah difabrikasi, dapat dituang (dengan
segala macam proses penuangan), dibentuk (dengan berbagai macam proses pembentukan dan tingkat deformasi), dimachining
• Wrought Alloy designation:
Major alloying element Alloy designation
Pure aluminium, 99,00 % and greater 1xxx
Copper 2xxx
Manganese
Silicon
Magnesium
Magnesium and silicon
Zinc
Other element
3xxx
4xxx
5xxx
6xxx
7xxx
8xxx
Merah : dapat dikeraskan dengan heat treatment (age hardenable)
Hitam : paduan yang non age hardenable
• Age hardening (precipitation hardening):– Terdiri dari dua tahapan:
1. Solution treatment; memanaskan sampai paduan menjadi single phase kemudian didinginkan cepat
2. Aging : - natural aging; membiarkan pada
temperatur kamar beberapa saat
- artificial aging; memanaskan ke
suatu temperatur, ditahan disana beberapa saat lalu didinginkan
–
• Temper designation: kode berupa huruf dan angka yang ditempatkan dibelakang nama/kode paduan, menunjukkan perlakuan pada proses pembuatannya1. F : as fabricated2. O : as annealed, recrystallized3. H : Strain-hardened
–H1 : strain-hardened only–H2 : Strain-hardened then partially annealed–H3 : Strain-hardened then stabilized
4. W : Solution Heat treated5. T : Thermally treated
1. T2 : Annealed2. T3 : Solution heattreated then cold-worked3. T4 : Solution heattreated and naturally aged to a
substantially stable condition4. T5 : Artificially aged only5. T6 : Solution heattreated then artificially aged6. T7 : Solution heattreated then stabilized7. T8 : Solution heattreated, cold worked then
artificially aged8. T9 : Solution heattreated artificially aged then
cold worked9. T10: Artificially aged then cold worked
• Aluminium copper (seri 2xxx)
mengandung 2,5 – 5,0 % Cu, dapat dikeraskan
- 2017 (duralumin), mengandung 4 % Cu,
digunakan untuk paku keling pada konstruksi
pesawat terbang
- 2014•
Pengerasan presipitasi pada paduan Al-4%Cu, menunjukkan perubahan selama pemanasan/pendinginan