Perlu atas pertimbangan yg berhub.dgn : * Besarnya RDT (Remaining Dentin Tickness) dan tebalnya atap pulpa * Jenis restorasi * Bahan adhesif Dentin & restorasi Terletak antara Pulpa & restorasi
Base → “High Strength Base”
Lapisan bahan dengan tebal antara 1-2 mm Digunakan untuk memberi :
• Perlindungan pada pulpa dari termal & kimia• Tambahan dukungan mekanik untuk restorasi
Bahan yg digunakan dicampur sampai mendapatkan konsistensi sekunder
Macam-macam bahan untuk base : - Semen Glass Ionomer - Hybrid ionomer - Polymer reinforced ZOE - Zinc phosphate - Zinc polycarboxilate
Campuran konsistensi dempul
Penggunaan Dental Cement
Proteksi pulpa : - Cavity varnish - Liner (low strength base) - Base (High strength base) - Build up Luting cementation : - Ortodontic band & brackets Restoration : - Permanent - Temporary - Intermediate Surgical dressing
Liner (Low strength base) Biasa disebut sebagai “Sub base”
Fungsi : - Sebagai barrier terhadap iritasi kimia - Memberi manfaat terapeutik pada pulpa Sediaan : * Ca(OH)2
* GIC * ZOE
Pulpa tidak tertutup dentin (perforasi atap pulpa tembus ke ruang pulpa)
Pulpa masih tertutup dentin tetapi sudah tipis (indirect pulp capping)
Komposisi : base & katalis atau powder & liquid
Kalsium hidroksida → pH 9 -12 (alkalis) Merangsang pembentukan dentin sekunder (direct
pulp capping) Sebagai barrier pelindung di bawah restorasi
komposit → tidak mengganggu polimerisasi
Fungsi proteksi pulpa, untuk mencegah rangsang:- kimia - mekanik- elektrik - medikasi pulpa- termal
base katalis
- Kalsium tungsten
- Kalsium fosfat
- Zinc oxide → Glical salisilat
- Ca(OH)2
- Zinc oxide- Zinc stearat (etilene toluene
sulfonamide)
Cavity Varnish & LinerVarnish → bukan semen tetapi dipakai bersama semen Resin alami (copal) atau resin sintetik Dilarutkan dalam pelarut spt : alkohol & kloroform
Fungsi cavity varnish & liner :
1. Sebagai barrier pelindung antara dentin & bahan restorasi
2. Mengurangi penetrasi iritan kimia yg terdapat pada bahan restorasi
3. Mengurangi mikroleakage & perubahan warna pada interface gigi yang direstorasi
4. Memberi efek terapeutik pada pulpa gigi
●
●
Mechanical properties of high & low strength bases
Cement
Compressive Strength
(MPa)
Tensile Strength
(MPa)
Modulus of Elasticity
(GPa†)
High strength bases
• Glass ionomer• Hybrid ionomer• Polymer reinforced ZOE (Tipe III)
• Zinc phosphate• Zinc polycarboxilate
70-210
150-200
38
130-160
80
3.9-8.3
20-40
3.4
8
16
3.7-9.0
8-20
2.1
22
5.0
Low strength bases
• Ca(OH)2 (light-cured)• Ca(OH)2 (self-cured)• ZOE (tipe IV)
96
12-26
5.5
38
1.0
0.4
-
0.4
0.3
Cement Product Manufacturer
• Glass ionomer• Hybrid ionomer
• Polymer reinforced • ZOE (Tipe III)• Zinc phosphate• Zinc polycarboxilate
Ketac-Bond Aplicap
Fuji II LC
Vitremer
Prime & Bond NT
Zinc cement
Durelon
3M ESPE (st.Paul, MN)
GC America (Alsip, IL)
3M ESPE
Dentsply/Caulk Milford, DE
Mission/Mizzy (charleston,SC)
3M ESPE
Low strength bases
•Ca(OH)2 (light-cured)• Ca(OH)2 (self-cured)• ZOE (tipe IV)
Dycal VLC
Dycal
Alumina super EBA
Cavitec
Dentsply /Caulk
Dentsply /Caulk
Boswoth (Skokie, IL)
SDS Kerr (Orange,CA)
Purpose CementHigh strength bases
Low strength bases
Ca(OH)2, GIC, ZOE Cement
Reinforced ZOE, ZP, Zinc Poly, GIC
Permanent cementation : Cast crown Porcelain, ceramic or
composite veneers,
inlays, onlays, & crowns Orthodontic bands Orthodontic brackets
ZP, Z.Poly, GIC, Hybrid GI, resin based
Resin based
Fluoride added to ZP, GIC
Resin based
Provisional restoration Reinforced ZOE, Polycarboxilate, ZP
Surgical dressing Eugenol & noneugenol surgical dressing
DAFTAR PUSTAKA
1. Mount GJ, Hume WR. Preservation and restoration of tooth structure. Mosby Int. Ltd. London (1998), p. 180 - 42. Hatrick CD, Eakle WS, Bird WF. Dental Material : Clinical applications for dental assistans and dental hygienists. Saunders St. Louis (2003), p. 172 – 843. Roberson TM, Heyman HO, Swift EJ. Sturdevant’s : Art and science of operative dentistry, 4 ed , Mosby, Inc. London (2002), p. 170 – 4, 217 – 204. Craig RG, Powers JM, Wataha JC. Dental materials properties and manipulation, 8 ed , Mosby, Inc. London (2004), p. 132 – 53